ML 5554 AlMg2,7Mn

典型成分%

Si <0,25
Fe <0,40
Cu <0,10
Mn 0,50-1,00
Mg 2,40-3,00
Cr 0,05-0,20
Zn <0,25
Be <0,0003
Ti 0,05-0,20
Others <0,05
Others, total <0,15

分类

EN ISO 18273  :  S Al 5554 ( AlMg2,7Mn )
Matériel Nr  :  3.3538
AWS A 5-10  :  ER 5554

基础材料

See table

注意

This alloy was developed for applications at high temperatures and for resistance against intergranular corrosion. Joining of the base metal 5454 with alloys of the 6000 range is possible. The weld metal is sea water resistant. Consider the technological application reference.

纯焊缝金属的物理性能 (Approx. values)

0,2 % yield strength Rp0,2 [MPa]  :  100
Tensile strength Rm [MPa]  :  25
Elongation A5 ( L0=5d0 ) [%]  :  17
Test temperature [°C]  :  20

焊接位置

PA, PB, PC, PF

保护气体

I1, I2, I3 (Argon, Helium or Argon/Helium-mixtures)

极性

MIG =+, WIG ~

批准

On request

尺寸

MIG-wires [mm]  :  0,8 ; 1,0 ; 1,2 ; 1,6 ; 2,0 ; 2,4
TIG-rods [mm]  :  1,6 ; 2,0 ; 2,4 ; 3,2 ; 4,0

焊丝包装材料

Spools  :  Packaging units

S 100 / 0,5 kg  :  20 spools = 10 kg (box)
S 200 / 2 kg  :  4 spools = 8 kg (box)
S 300 / 6 kg  :  84 spools = 504 kg (pallet)
B 300 / BS 300 / 7 kg  :  84 spools = 588 kg (pallet)
B 400 / 18 kg  :  28 spools = 504 kg (pallet)
B 400 / 40 kg  :  15 spools = 600 kg (pallet)
Fût / 80 kg  :  2 drums = 160 kg (pallet)
Fût Jumbo / 140 kg  :  2 drums = 280 kg (pallet)

焊条包装材料

Carton 5 kg ; carton 10 kg  :  Length 1.000 mm